Abstract process experimental period of nearly two years of production and that the fluoroboric acid system to 2,4-- dichlorobenzaldehyde as Additive Sn-Pb alloy plating mirror bright, process stability. Jiaxing Ganland Excavator aftermarket Cabs for Komatsu ,Hitachi, CAT, Doosan, Kobelco, Daewoo, Hyundai, Volvo, Kubota, Sumitomo,Deere, Case, Linkbelt, etc. We have so many cabins for so many different types, models and series. You can just send me what you need, I will show you what we have. If you have time visit China, you are very welcome to coming to our factory. You will find our products are with high quality and also cheap price. MOQ is 1 piece. Excavator Cabs for Aftermarket Komatsu,Excavator Cabs for Aftermarket Hitachi, Excavator Cabs for Aftermarket Doosan, Excavator Cabs for Aftermarket Kobelco Jiaxing Ganland Auto Parts Co., Ltd. , https://www.ganlandparts.com
I products are more silver plated member, but after a period of time is placed silver black, solderability and resistivity will be greatly affected. After DJB-823 is applied, its appearance is affected, and it is necessary to have conductivity under a certain pressure. Therefore, it is imperative to develop a silver-based material.
At that time, many reports that Sn-Ce alloy was a better silver substitute material, we started this process test, but the effect was not satisfactory. So we developed the bright Sn-Pb process, first around the purchase of commercial additives test, but the effect is not ideal, mainly because the coating is not bright, the solution is unstable, so we checked the data and in-depth test, finally found a comparison Good process specifications, after two years of trial production, the performance is quite stable. There are no additives in almost two years, but always keep the high current plating and plating mirror bright. Today I will introduce the work of these years to everyone, I hope everyone can benefit from it. .
1 Process specification
1.1 Process recipe Sn 2+ 18-25g/l
Pb 2+ 8-11g/l
HBF 4 (free) 250-300g/l
H 3 BO 3 : 10-30g/l
OP21 10-30g/l
2.4-dichlorobenzaldehyde lg/l
O-toluidine 6-10ml/l
HCHO 5-15g/l
Dk 5-15A/dm 2
Cathode movement 40-60 times / min
Tem room temperature 1. 2 process
Pretreatment - copper cyanide base - cleaning - plating Sn - Pb - cleaning - passivation - cleaning - drying - inspection [next]
1.3 Precautions 1.3.1 Additives Add 2,4-dichlorobenzaldehyde to o-toluidine for a period of time, then add OP21, HCHO can be added to the bath separately.
1.3.2 The workpiece should not be placed too dense to prevent local fogging.
1.3.3 If the bath has not been used for a long time, test the current density range with HULL before plating.
1.3.4 The coating is bright, so it is supplemented by high-speed cathode movement.
1.3.5 Suitable for iron and copper alloy substrates.
1.3.6 Unqualified plating removal is carried out in the usual way.
2 plating quality inspection
2.1 Appearance The coating is blue with a mirror finish.
2.2 Bonding force according to SJ1282—73 qualified 2.3 third-order performance
Execution according to GJB367, 2-87, wet heat and salt spray test, qualified 2.4 welding performance
Better than silver plating, good fluidity.
3, Conclusion <br> The process has been put into production in 1995, the effect is very good, the coating mirror is bright, and the efficiency is very high, for high-current electroplating, generally plating for 5-10 minutes, from the solution to the present, has not been adjusted once and supplemented The additive proves that the performance of the plating solution is extremely stable. The disadvantage is that the plating solution is a fluoroboric acid system, which has certain requirements for environmental protection, but the process is much better than the many additives at home and abroad in terms of production, which is us. Do a lot of conclusions from comparative experiments.
References 1, Zeng Hualiang, etc., "Electroplating Process Manual" Machinery Industry Press 1993
2, (United States) Frederick "Modern Electroplating" Machinery Industry Press 1982
3. Chen Lizhen, Tsinghua University Science Report, 1979